Chemical composition % of steel C35E (1.1181): EN 10277-5-2008
Cr + Mo + Ni = 0.63
CSiMnNiPSCrMo
0.32 - 0.39max 0.40.5 - 0.8max 0.4max 0.03max 0.035max 0.4max 0.1

New opportunities for buyers!
Post free buying requirement of steel C35E (1.1181)


Mechanical properties of steel C35E (1.1181)

Nominal thickness (mm):to 1616 - 100100 - 250250 - 500500 - 1000






Rm - Tensile strength (MPa) (+N)550520500480470
Nominal thickness (mm):0.3 - 3


Rm - Tensile strength (MPa) (+A)540
Nominal thickness (mm):0.3 - 3


Rm - Tensile strength (MPa) (+CR)930
Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






Rm - Tensile strength (MPa) (+C)650-1000600-950580-880550-840520-800
Nominal thickness (mm):to 88 - 2020 - 5050 - 80





Rm - Tensile strength (MPa) (+QT)630600550500


Nominal thickness (mm):to 88 - 2020 - 5050 - 80





ReH - Minimum yield strength (MPa) (+QT)430380320290


Nominal thickness(mm):to 1616 - 100100 - 250




Re - Upper yield strength or
Rp0.2 - 0.2% proof strength (MPa) (+N)		300270245
Nominal thickness(mm):0.3 - 3


Rp0.2 0.2% proof strength (MPa) (+A)430
Nominal thickness(mm):to 100100 - 250250 - 500500 - 1000





Re - Upper yield strength (MPa) (+N)270245220210
Nominal thickness(mm):5 - 1010 - 1616 - 4040 - 6363 - 100






Rp0.2 0.2% proof strength (MPa) (+C)510420320300270




KV - Impact energy (J) (+QT)+20°
35


KV - Impact energy (J) (+N)+20°
27


KV - Impact energy (J) transverse, (+QT)+20°
22




A - Min. elongation at fracture (%) transverse, (+N)15
Nominal thickness (mm):5 - 1010 - 1616 - 4040 - 6363 - 100






A - Min. elongation at fracture (%) (+C)67899
Nominal thickness (mm):to 88 - 2020 - 5050 - 80





A - Min. elongation at fracture (%) longitud., (+QT)17192020


A - Min. elongation at fracture (%) longitud., (+N)21


A - Min. elongation at fracture (%) longitud., (+A)22


Nominal thickness (mm):to 1616 - 100100 - 250




A - Min. elongation Lo = 5,65 √ So (%) (+N)181919


Brinell hardness (HBW): (+SH)154 - 207
Brinell hardness (HBW): (+A)183
Vickers hardness ( HV): (+CR)275
Vickers hardness ( HV): (+A)170


Properties of steel C35E (1.1181)
Weldability: It can be welded quite well without any precautions.
Hardenability: Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all nonalloy steels with medium-high carbon content.


Equivalent grades of steel C35E (1.1181)
Warning! Only for reference
EU
EN		USA
-		Germany
DIN,WNr		Japan
JIS		France
AFNOR		England
BS		Italy
UNI		Spain
UNE		China
GB		Sweden
SS		Finland
SFS		Russia
GOST		Inter
ISO
C35E
1035
Ck35
S35C
XC38
XC38H1
080M36
CFS6
C35
C35k
F1130
35
1572
C35
35
C35E4